FLOOR LEVEL HP THERM is a self-levelling modified-polymer cement mortar having fibre-reinforcement, with high thermal conductivity, fast-acting hold and rapid hardening. Applied prior to laying the flooring, it is perfect for levelling at thicknesses ranging from 3 mm to 15 mm so as to adapt to any type of covering. Particularly suitable for radiant flooring.
Material para betonilhas
Conservação: 12 meses
Diâmetro máximo agregado: 0.5 mm
Espessura máxima recomendada: 20 mm
Espessura mínima recomendada: 3 mm
Misturar com água: 20 %
Pot-life: 20 min
Resistentes aos raios UV
Temperatura de uso: +5/+35 °C
Conteúdo de cloretos
< 0.01 %
Ligação de aderência
> 2 MPa
Módulo elástico estático
Permeabilidade ao vapor de água
> 12 _
Resistência à compressão aos 01 dia
> 4 MPa
Resistência à compressão aos 28 dias
> 38 MPa
Resistência à flexão aos 28 dias
> 9 MPa
Resistência à flexão em 01 dia
> 3 MPa
Tempo de presa
- Saco 25 kg
The perfect pourability, fluidity and self-levelling properties of the mortar facilitate the coating operations, to quickly attain perfect planarity. By casting the product on the substrate and helping to spread the self-levelling product with a putty knife, the resulting surface is perfectly smooth thanks to the fine granulometry of the silica aggregate (with a maximum size of 0.5 mm). FLOOR LEVEL HP THERM is additivated with shrinkage reducers and fibre-reinforced with special anti-cracking glass microfilaments, being alkali resistant and with a high content of zirconium (READYMESH technology), metal microfibres 6 millimetres in length, and iron-silicate microaggregates with high volumic mass, all to confer exceptional dimensional stability to the product. As an additive, FLOOR LEVEL HP THERM has a special high-flexibility powder adhesive that ensures the product bonds to various media without affecting the self-levelling characteristics and breathability to water vapour. The swift development of mechanical resistors ensures the immediate progression of construction operations and walkability just a few hours after application (approximately 4-5 hours at 20° C). Fast drying means the floor coverings and finishing operations can be applied sooner – always checking the moisture content of the hardened mortar with a calcium carbide hygrometer or electrical hygrometer and bearing in mind that the latter provides merely indicative values that should be calibrated on the product in advance.
Approximately 1.8 kilograms/square metre of FLOOR LEVEL HP THERM is needed for every millimetre of thickness to be achieved.
FLOOR LEVEL HP THERM can be used to shave uneven substrates to be levelled then subsequently covered with various types of flooring (ceramic tiles, marble, wood, plastic material, and so on), especially in cases where speed of execution is required and the finished flooring needs high resistance to loads and heavy traffic, along with high thermal conductivity and extensive levelling density. Some substrate examples include:
• concrete slabs and cement screeds;
• anhydrite substrates; • heated floors;
• existing concrete flooring, terrazzo tiles, natural stones, magnesite.
• existing ceramic flooring with the substrates subject to priming with two-component SYNTECH RGS resin (consumption approximately 1.2 kilograms/m2) and casting of FLOOR LEVEL HP THERM on wet resin.
Also suitable for particularly stressed areas of application, such as foundations subjected to intense dynamic-vibrational stress.
The surfaces on which the product is to be applied must be cleaned of dust, free from contamination, paints, loose and crumbly parts, and so on. Adopt effective mechanical measures to remove residues that could impact upon product adhesion. On media with standard absorption, slightly wet the substrate with water to clean the surface and favour the bonding of FLOOR LEVEL HP THERM. If the substrate is particularly absorbent, weak and crumbly or whereby it is not possible to slightly wet, prime the surfaces with the special aqueous resin dispersion BOND PLUS, preferably spreading the product with a rigid-bristle brush to promote penetration into the base. In all cases where surfaces are primed with BOND PLUS, the application of FLOOR LEVEL HP THERM must take place “wet-on-wet” immediately after the first priming — with a consumption of BOND PLUS at about 200 grams/square metres. On non-absorbent, vitrified, ceramised bases – such as ceramic or klinker tiles – prime surfaces with the bicomponent SYNTECH RGS resin (with a consumption of 1.2 kilograms/m2) and apply FLOOR LEVEL HP THERM onto the resin whilst still fresh. FLOOR LEVEL HP THERM is pumpable but, since the product has accelerated grip, the casting must be continuous and without interruption (with the pump to be entirely emptied before any stoppage to the pumping lasting more than 10 minutes).
Mix with a triple-helix paddle with a high rotational count or with a vertical axis mixer. Put 2/3 of the total water for the mixture into the mixer, gradually adding the product and the remaining water, stirring for about 2–3 minutes until obtaining a homogeneous mixture with castable consistency. The mixture must contain from 18% to 20% water by weight (from 4.5 litres to 5.0 litres per 25-kilogram bag). Strain the mixture thus obtained onto the substrate and spread with a rubber blade, standard metal putty knife or toothed trowel (angled to obtain the desired thickness). Thanks to its perfect self-levelling characteristics, FLOOR LEVEL HP THERM immediately fills the grooves left by the toothed trowel and eliminates small imperfections caused by its passage (trowel markings). Finish the adjustment and smoothing operations within 20 minutes. The product has accelerated grip and hardening, meaning there should be no pause between mixing and application. The product cures in around 45 minutes and is walkable after a few hours.
- Espátula dentada
- Azulejos e pisos
- Betonilhas de substrato
- Pedras naturais